For non-magnum pistol rounds I've found that straight COWWs is entirely satisfactory. I used to use a #2 type alloy for handgun rounds and still keep some around. I used it because the added tin seemed to make casting easier but have found out that mold temperature makes more difference to filling out well. Wouldn't hesitate to use it if I needed to but usually don't need it.
Other folks here know a lot more about alloys for high pressure loads, but I try not to overthink things for casual handgun shooting.